Calcinable refractario moldeable con alto contenido de alúmina

1.Excellent abrasion resistance
2.Excellent high-temperature resistance
3.Excellent Crushing Strength
4.Anti-corrode

Categorías: Moldeable con alto contenido de alúmina, Materiales refractarios sin forma

Descripción del Producto

High Alumina castable is mixed by high quality bauxite, Mullita, andalusite or Corundum as aggregate, Silica Powder, α-alumina powder as micro powder, refractory cement as binder, also some additive to make better performance. Formulas are changed according to different applications.
Comparing to conventional dense castable, high alumina castable can be used in the area that have more higher temperature and also have higher cold crushing strength.

Parámetro

Artículo	LAHA75	LAHA80	LAHA85	LAHA95
Temperatura de servicio ℃	1600	1650	1700
Densidad a Granel (g/cm3)	2.5	2.6	2.7	3
(Secado a 110 ℃)	2.5	2.6	2.7	3
CCS 110 ℃	65	70	90	95
(MPa) 1100℃	55	60	80	85
1500 ℃	80	85	100	110
MOR 110℃	10	11	12	13
(MPa) 1100℃	9	9	10	12
1500℃	11	12	13	15
Tamaño máximo de grano (milímetro)	6	6	6	6
Análisis químico(%)
Al2O3	75	80	85	95
Fe2O3	2.5	2	1.8	1.2
Pautas de aplicación
Mezclador	PAG	PAG	PAG	PAG
Colocación	VERMONT	VERMONT	VERMONT	VERMONT
Temperatura del agua/mezclador ℃	20±5	20±5	20±5	20±5
Tiempo de mezcla(mínimo):Seco húmedo	2/5	2/5	2/5	2/5
Agua % (Típico)	7-9	7-9	7-9	7-9